RTV-2 Tin Cure Silicone (Condensation Cure) for Cylindrical Cup Mold Calculator
Pre-loads specific gravity (1.12) and 10:1 mix ratio to calculate exact Part A & Part B weights with cup scraping buffer.
A standard Cylindrical Cup Mold (Ø9 × 12 cm minus 150 cm³ master) requires 742g (26.17 oz / 1.64 lbs) of RTV-2 Tin Cure Silicone (Condensation Cure). Mix 674.5g Part A with 67.5g Part B (8% buffer included).
Casting Material & Volume Mode
Pre-loads specific gravity and 10:1 ratio by weight.
Geometry determines the container-volume formula. Use water displacement when the cavity is irregular.
Volume displaced by your master object inside the box.
Compensates for resin clinging to mixing paddles and cup walls (8% recommended).
Includes 8% waste buffer at SG 1.12
Ratio part: 10
Ratio part: 1
Net volume before buffer
Order RTV-2 Tin Cure Silicone (Condensation Cure) Kit
High-tear strength RTV-2 Tin Cure Silicone (Condensation Cure) with verified 10:1 ratio. Ideal for bubble-free casting.
RTV-2 Tin Cure Silicone (Condensation Cure) vs Alternative Casting Compounds
Compare specific gravities, mix ratios, working times, and cure speeds across casting compounds.
| Material / Specification | Specific Gravity | Mix Ratio | Pot Life | Demold Time |
|---|---|---|---|---|
| RTV-2 Tin Cure Silicone (Condensation Cure)ACTIVE | 1.12 | 10:1 (weight) | 45 min | 12 hrs |
| RTV-2 Platinum Silicone (Smooth-On Mold Star 15/30) | 1.07 | 1:1 (weight) | 30 min | 6 hrs |
| Jesmonite AC100 (Eco-Resin) | 1.75 | 2.5:1 (weight) | 12 min | 2 hrs |
| Jesmonite AC730 (Stone Casting) | 1.85 | 5:1 (weight) | 15 min | 4 hrs |
| Deep Pour River Epoxy (2:1 Ratio) | 1.11 | 2:1 (weight) | 90 min | 48 hrs |
| Table Top & Art Epoxy (1:1 Ratio) | 1.08 | 1:1 (weight) | 25 min | 12 hrs |
Step-by-Step Mix Ratio Derivation: RTV-2 Tin Cure Silicone (Condensation Cure)
How displacement volume, specific gravity, and ratio split combine into final scale weights.
Calculates the empty fluid cavity by taking the gross 763.4 cm³ cylinder containment volume and deducting the 150 cm³ displaced by the master model.
Multiplies fluid volume by the specific gravity of RTV-2 Tin Cure Silicone (Condensation Cure) (1.12 g/cm³) plus an 8% buffer for cup scraping and pouring loss.
Distributes batch mass according to the exact 10:1 ratio by weight.
Engineering Specifications & Troubleshooting Guide: RTV-2 Tin Cure Silicone (Condensation Cure)
Factory-tested parameters, common failure modes, and workbench best practices.
- Immune to cure inhibition from sulfur clays and UV 3D resins; ideal when making molds of photopolymer resin 3D prints.
- Has slightly higher linear shrinkage (0.2% - 0.4%) than platinum cure.
- Measure Part B on a precision gram scale (0.1g accuracy) because the 10:1 ratio is sensitive to catalyst ratios.
Eyeballing Part B catalyst; adding too much causes brittleness, too little leaves the silicone permanently tacky.
Frequently Asked Questions: RTV-2 Tin Cure Silicone (Condensation Cure)
Mix ratios, degas guidelines, cure times, and mold making tips.
Q1What is the mix ratio of RTV-2 Tin Cure Silicone (Condensation Cure)?
Q2How much RTV-2 Tin Cure Silicone (Condensation Cure) do I need for a Cylindrical Cup Mold?
Q3How long before I can demold RTV-2 Tin Cure Silicone (Condensation Cure)?
Next Step In Your Project (Companion Fabrication Tools)
Pair your current build with companion engineering calculators: